Shot Azzar
Kompożizzjoni Kimika | C | 0.85-1.20% |
Si | 0.40-1.20% | |
Mn | 0.60-1.20% | |
S | ≤0.05% | |
P | ≤0.05% | |
Ebusija | HRC 40-50 | |
Mikrostruttura | Martensite jew Troostite Ttemprat Omoġenju | |
Densità | ≥ 7.2g/cm3 | |
Forma esterna | Sferika Partiċelli vojta <10% |
Distribuzzjoni tad-daqs
Screen Nru. | Pulzier | Daqs tal-iskrin | S70 | S110 | S170 | S230 | S280 | S330 | S390 | S460 | S550 | S660 | S780 | S930 |
6 | 0.132 | 3.35 | Kollha jgħaddu | |||||||||||
7 | 0.111 | 2.80 | Kollha jgħaddu | |||||||||||
8 | 0.0937 | 2.36 | Kollha jgħaddu | ≥90% | ||||||||||
10 | 0.0787 | 2.00 | Kollha jgħaddu | Kollha jgħaddu | ≥85% | ≥97% | ||||||||
12 | 0.0661 | 1.70 | Kollha jgħaddu | ≤5% | ≥85% | ≥97% | ||||||||
14 | 0.0555 | 1.40 | Kollha jgħaddu | ≤5% | ≥85% | ≥97% | ||||||||
16 | 0.0469 | 1.18 | Kollha jgħaddu | ≤5% | ≥85% | ≥97% | ||||||||
18 | 0.0394 | 1.00 | Kollha jgħaddu | ≤5% | ≥85% | ≥96% | ||||||||
20 | 0.0331 | 0.850 | Kollha jgħaddu | ≤10% | ≥85% | ≥96% | ||||||||
25 | 0.0280 | 0.710 | ≤10% | ≥85% | ≥96% | |||||||||
30 | 0.0232 | 0.600 | Kollha jgħaddu | ≥85% | ≥96% | |||||||||
35 | 0.0197 | 0.500 | ≤10% | ≥97% | ||||||||||
40 | 0.0165 | 0.425 | Kollha Għaddi | ≥85% | ||||||||||
45 | 0.0138 | 0.355 | ≤10% | ≥97% | ||||||||||
50 | 0.0117 | 0.300 | ≥80% | |||||||||||
80 | 0.007 | 0.180 | ≥80% | ≥90% | ||||||||||
120 | 0.0049 | 0.125 | ≥90% | |||||||||||
200 | 0.0029 | 0.075 |
Applikazzjoni
Tindif tal-blast: Użat għat-tindif tal-blast ta 'ikkastjar, die-casting, forġa;tneħħija tar-ramel tal-ikkastjar, pjanċa tal-azzar, azzar tat-tip H, struttura tal-azzar.
Tneħħija tas-sadid: Tneħħija tas-sadid ta 'ikkastjar, forġa, pjanċa tal-azzar, azzar tat-tip H, struttura tal-azzar.
Shot peening: Shot peening ta 'rkaptu, partijiet ittrattati bis-sħana.
Sand blasting: Sand blasting ta 'azzar profil, bord tal-vapur, bord tal-azzar, materjal tal-azzar, struttura tal-azzar.
Trattament minn qabel: Trattament minn qabel tal-wiċċ, bord tal-azzar, azzar tal-profil, struttura tal-azzar, qabel iż-żebgħa jew il-kisi.